| Wire name | Standard | Diameter (mm) | Welding method | Hardness in 3 layers |
|---|---|---|---|---|
| CoWeld® 011 | EN 14700 T Fe10 200/50 CKPRZ | 1.2 – 2.8
1.2 – 2.4 1.6 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
180 HB,
after hardening: 48 HRC |
| CoWeld® 012 | EN 14700 T Fe9 250/50 CKNPR | 1.2 – 2.8
1.2 – 2.4 1.6 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
280 HB,
after hardening: 45–50 HRC |
| CoWeld® 013 | EN 14700 T Fe9 200/50 KNP | 1.2 – 2.8
1.2 – 2.4 |
O – Self-shielded
G – Gas-shielded |
200 HB,
after hardening: 42–48 HRC |
| Wire name | Standard | Diameter (mm) | Welding method | Hardness in 3 layers |
|---|---|---|---|---|
| CoWeld® 021 | EN 14700 T Fe1 250 P | 1.2 – 2.8
1.2 – 2.4 1.6 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
260 HB |
| CoWeld® 022 | EN 14700 T Fe1 350 P | 1.2 – 2.8
1.2 – 2.4 1.6 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
360 HB |
| CoWeld® 023 | EN 14700 T Fe1 400 P | 1.2 – 2.8
1.2 – 2.4 1.6 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
400 HB |
| CoWeld® 024 | EN 14700 T Fe2 55 GSP | 1.2 – 2.8
1.2 – 2.4 1.6 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
56–59 HRC |
| CoWeld® 025 | EN 14700 T Fe1 250 P | 1.2 – 2.4 | G – Gas-shielded | 250 HB |
| CoWeld® 026SP | EN 14700 T Fe1 350 P | 1.2 – 2.4 | G – Gas-shielded | 350 HB |
| CoWeld® 027SP | EN 14700 T Fe1 45 SP | 1.2 – 2.4 | G – Gas-shielded | 450 HB |
| CoWeld® 028SP | EN 14700 T Fe2 55 GSP | 1.2 – 2.4 | G – Gas-shielded | 57–59 HRC |
| CoWeld® 029SP | EN 14700 T Fe3 60 GPZ | 1.2 – 1.6 | G – Gas-shielded | 59–62 HRC |
| Wire name | Standard | Diameter (mm) | Welding method | Hardness in 3 layers |
|---|---|---|---|---|
| CoWeld® 031 | EN 14700 T Fe3 45 SPT | 1.2 – 2.8
1.2 – 2.4 1.6 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
45 HRC |
| CoWeld® 032 | EN 14700 T Fe3 55 GST | 1.2 – 2.8
1.2 – 2.4 1.6 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
55 HRC |
| CoWeld® 033 | EN 14700 T ZFe 45 SPT | 1.2 – 2.4 | G – Gas-shielded | 35 HRC |
| CoWeld® 034 | EN 14700 T Fe3 45 SPT | 1.2 – 2.4 | G – Gas-shielded | 45 HRC |
| CoWeld® 035 | EN 14700 T Fe3 50 SPT | 1.2 – 2.4 | G – Gas-shielded | 53 HRC |
| CoWeld® 039 | EN 14700 T Fe4 60 ST | 1.2 – 2.4 | G – Gas-shielded | 60 HRC
Hardness can be increased to 65 HRC by heat treatment |
| CoWeld® 0310 | EN 14700 T ZFe3 45 CRTZ | 1.2 – 2.8
1.2 – 2.4 1.6 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
45–50 HRC |
| CoWeld® 0311 | EN 14700 T ZFe3 45 SPT | 1.2 – 1.6 | G – Gas-shielded | 44 HRC Heat treatment
550°C / 10 h: 48 HRC |
| CoWeld® 0312 | EN 14700 T ZFe3 45 SPT | 1.2 – 1.6 | G – Gas-shielded | 43 HRC Heat treatment
550°C / 10 h: 46 HRC |
| CoWeld® 0313 | EN 14700 T ZFe3 55 SPT | 1.2 – 1.6 | G – Gas-shielded | 53 HRC Heat treatment
550°C / 10 h: 55 HRC |
| CoWeld® 0314 | EN 14700 T ZFe3 35 SPT | 1.2 – 1.6 | G – Gas-shielded | 35 HRC Heat treatment
550°C / 10 h: 38 HRC |
| CoWeld® 0315 | EN 14700 T ZFe3 45 SPT | 1.2 – 1.6 | G – Gas-shielded | 45 HRC Heat treatment
550°C / 10 h: 50 HRC |
| CoWeld® 0316 | EN 14700 T ZFe3 50 SPT | 1.2 – 1.6 | G – Gas-shielded | 49 HRCHeat |
| Wire name | Standard | Diameter (mm) | Welding method | Hardness in 3 layers |
|---|---|---|---|---|
| CoWeld® 041 | EN 14700 T ZFe13 65 G | 1.2 – 2.8 | O – Self-shielded | 65 HRC |
| CoWeld® 042 | EN 14700 T ZFe13 65 GT | 1.2 – 2.8 | O – Self-shielded | 64–68 HRC |
| CoWeld® 043 | EN 14700 T ZFe14 60 GC | 1.2 – 2.8 | O – Self-shielded | 60 HRC |
| CoWeld® 044 | EN 14700 T Fe15 60 GCZ | 1.2 – 2.8 | O – Self-shielded | 60–62 HRC |
| CoWeld® 045 | EN 14700 T Fe14 60 GCZ | 1.6 – 2.8 | O – Self-shielded | 60–62 HRC |
| CoWeld® 046 | EN 14700 T Fe15 65 GCZ | 1.6 – 2.8 | O – Self-shielded | 62–64 HRC |
| CoWeld® 047 | EN 14700 T Fe16 65 GCZ | 1.6 – 2.8 | O – Self-shielded | 63–67 HRC |
| CoWeld® 048 | EN 14700 T Fe16 65 GCZ | 1.6 – 2.8 | O – Self-shielded | 65–67 HRC |
| CoWeld® 049 | EN 14700 T Fe20 50 GR | 1.6 – 2.8 | O – Self-shielded | Tungsten carbides: 2360
HVMatrix: martensite / approx. 42 HRC |
| CoWeld® 0410 | EN 14700 T Ni20 50 CGRZ | 1.6 – 2.8 | G – Gas-shielded | Tungsten carbides: 2360
HVMatrix: Ni–Cr–B–Si / 500–600 HV |
| CoWeld® 0410W | EN 14700 T Ni20 50 CGTZ | 1.6 – 2.8 | G – Gas-shielded | Tungsten carbides: 3000
HVMatrix: Ni–Cr–B–Si / 500–600 HV |
| CoWeld® 0410Co | EN 14700 T Ni20 50 CGTZ | 1.6 – 2.8 | G – Gas-shielded | Tungsten carbides: 1950
HVMatrix: 450–480 HV |
| Wire name | Standard | Diameter (mm) | Welding method | Hardness in 3 layers |
|---|---|---|---|---|
| CoWeld® 051 | EN 14700 T Fe7 CZ | 1.6; 2.4
1.2 – 2.4 2.4 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
220 HB |
| CoWeld® 052 | EN 14700 T Fe7 CZ | 1.6; 2.4
1.2 – 2.4 1.6 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
42 HRC |
| CoWeld® 053 | EN 14700 T Fe7 CZ | 1.6; 2.4
1.2 – 2.4 1.6 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
40 HRC |
| CoWeld® 054 | EN 14700 T Fe8 C | 1.6; 2.4
1.2 – 2.4 2.4 – 3.2 |
O – Self-shielded
G – Gas-shielded F – Submerged arc |
50 HRC |
| Wire name | Standard | Diameter (mm) | Welding method | Hardness in 3 layers |
|---|---|---|---|---|
| CoWeld® 061 | EN 14700 T Co3 | 1.2 – 2.4 | G – Gas-shielded | 53 HRC
Higher deposition rate and lower dilution are achieved by pulsed welding |
| CoWeld® 066 | EN 14700 T Co2 TZ | 1.2 – 2.4 | G – Gas-shielded | 45 HRC
Higher deposition rate and lower dilution are achieved by pulsed welding |
| CoWeld® 063 | EN 14700 T Co2 TZ | 1.2 – 1.6 | G – Gas-shielded | 46 HRC
Higher deposition rate and lower dilution are achieved by pulsed welding |
| CoWeld® 064 | EN 14700 T Co1 CKTZ | 1.2 – 1.6 | G – Gas-shielded | after welding: 33 HRC
after hardening: 47 HRC |
| CoWeld® 065 | EN 14700 T ZCo1 CKTZ | 1.2 – 1.6 | G – Gas-shielded | after welding: 210 HB
after hardening: 40 HRC |
| CoWeld® 066LC | EN 14700 T Co2 TZ | 1.2 – 1.6 | G – Gas-shielded | 40 HRC
Higher deposition rate and lower dilution are achieved by pulsed welding |
| Wire name | Standard | Diameter (mm) | Welding method | Mechanical properties |
|---|---|---|---|---|
| CoWeld® 071 | EN ISO 1071 T C NiFe-2 | 1.2; 1.6 | G – Gas-shielded | Rm [MPa] 550
Rp0.2 [MPa] 340 A5% 16 Hardness 160 HB |
| CoWeld® 072 | EN ISO 1071 T C Z NiFe-1 M | 1.2; 1.6 | G – Gas-shielded | Rm [MPa] 470
Rp0.2 [MPa] 350 A5% 15 Hardness 180 HB |
| CoWeld® 073 | EN 14700 T Ni 6182 | 1.2; 1.6 | G – Gas-shielded | Rm [MPa] 610
Rp0.2 [MPa] 380 A5% 45 KCV [J] 90 @ –196°C |
| CoWeld® 074 | EN ISO 14172 T Ni 6625 | 1.2; 1.6 | G – Gas-shielded | Rm [MPa] 780
Rp0.2 [MPa] 500 A5% 40 KCV [J] 70 @ –196°C |