| Electrode name | Standard | Diameter (mm) | Mechanical properties |
|---|---|---|---|
| CoWeld® 312-E | EN 8555 E 9-UM-200-CTZ | 2,5×300
3,2×350 4,0×350 5,0×450 |
Rm [MPa] 800
Rp 0,2 [MPa] 580 A5% 20 hardness 200 HB |
| CoWeld® 312M-E | EN 8555 E 9-UM-200-CTZ | 2,5×300
3,2×350 4,0×350 5,0×450 |
Rm [MPa] 870
Rp 0,2 [MPa] 700 A5% 16 hardness 200 HB |
| CoWeld® 309MoL-E | EN ISO 3581-A E 23 23 2 L R 12 | 2,5×300
3,2×350 4,0×450 5,0×450 |
Rm [MPa] 650
Rp0,2 [MPa] 450 A5% 30 CV [J] 48 @ –20°C |
| CoWeld® F16-E | EN 14172 E Ni 6082 | 2,5×300
3,2×350 4,0×450 |
Rm [MPa] 700
Rp0,2 [MPa] 420 A5% 42 CV [J] 96 @ –196°C |
| Electrode name | Standard | Diameter (mm) | Mechanical properties |
|---|---|---|---|
| CoWeld® NiFe-E | AWS A 5.15 E NiFe-Cl | 2,5×300
3,2×350 4,0×350 |
Rm [MPa] 500
Rp0,2 [MPa] 350 A5% 10 hardness 190 HB |
| CoWeld® Ni-E | AWS A 5.15 E Ni-Cl | 2,5×300
3,2×350 4,0×350 |
Rm [MPa] 400
A5% 8 hardness 160 HB |
| CoWeld® NiCu-E | AWS A 5.15 E NiCu-B | 2,5×300
3,2×350 4,0×450 |
Rm [MPa] 400
Rp0,2 [MPa] 300 A5% 15 hardness 165 HB |
| Electrode name | Standard | Diameter (mm) | Hardness in 3 layers |
|---|---|---|---|
| CoWeld® 061-E | EN 14700 E Co3 | 3,2×350
4,0×450 5,0×450 |
20°C – 55 HRC
600°C – 44 HRC 800°C – 34 HRC |
| CoWeld® 062-E | EN 14700 E Co2 | 2,5×300
3,2×350 4,0×350 5,0×450 |
20°C – 42 HRC
300°C – 35 HRC 600°C – 32–39 HRC |
| CoWeld® 063-E | EN 14700 E Co3 | 2,5×300
3,2×350 4,0×350 5,0×450 |
20°C – 48 HRC
300°C – 37 HRC 600°C – 29 HRC |
| CoWeld® 064-E | EN 14700 E Co1 | 2,5×300
3,2×350 4,0×350 5,0×450 |
20°C – 30 HRC
300°C – 280 HB cold working– 45 HRC |
| Electrode name | Standard | Diameter (mm) | Hardness in 3 layers |
|---|---|---|---|
| CoWeld® 044-E | DIN 8555 E 10-UM-60-GR | 2,5×350
3,2×350 4,0×450 5,0×450 |
60–63 HRC |
| CoWeld® 047-E | DIN 8555 E 10-UM-65-GTRZ | 2,5×350
3,2×350 4,0×450 5,0×450 |
64 HRC |
| CoWeld® 048-E | DIN 8555 E 10-UM-65-GRZ | 3,2×450
4,0×450 5,0×450 |
64 HRC (20°C)
600 HV (550°C) |
| CoWeld® CX800-E | DIN 8555 E 10-UM-70-GTRZ | 3,2×450
4,0×450 5,0×450 |
68–70 HRC (20°C)
600 HV (800°C) |
| CoWeld® 049-E | DIN 8555 E 21-GF-UM-60-GP | 3,2×350
4,0×350 5,0×350 |
tungsten carbides 2360 HV
Matrix: martensite 62 HRC |
| CoWeld® 0410-E | DIN 8555 E 21-GF-UM-50-CG | 4,0×350
5,0×350 6,0×350 |
tungsten carbides: 2360 HV
Matrix Ni–Cr–B–Si: 500–600 HV |
| Electrode name | Standard | Diameter (mm) | Hardness in 3 layers |
|---|---|---|---|
| CoWeld® 026-E | EN 14700 E Fe 1 | 3,2×450
4,0×450 5,0×450 |
275–325 HB |
| CoWeld® 027-E | EN 14700 E Fe 7 | 3,2×450
4,0×450 5,0×450 6,0×450 |
375–420 HB |
| CoWeld® 028-E | EN 14700 E Fe 6 | 3,2×450
4,0×450 5,0×450 6,0×450 |
59–60 HRC |
| CoWeld® 600MoV-E | EN 14700 E Fe 6 | 3,2×450
4,0×450 5,0×450 |
59–62 HRC |
| Electrode name | Standard | Diameter (mm) | Hardness in 3 layers |
|---|---|---|---|
| CoWeld® 307B-E | DIN 8555 E 8-UM-200-CKNPZ | 2,5×300
3,2×350 4,0×450 5,0×450 |
180 HB after hardening 44 HRC |
| CoWeld® 012-E | DIN 8555 E 7-UM-250-KP | 3,2×350
4,0×450 5,0×450 |
280 HB after hardening 45–54 HRC |
| CoWeld® 013-E | DIN 8555 E 7-UM-250-KP | 3,2×350
4,0×450 5,0×450 |
250 HB after hardening 48–55 HRC |